鋳造用マグネシウム合金の化学組成と機械的性質

種 類

標準化学組成

(mass%)

質別

引張強さ

(MPa)

耐力

(MPa)

伸び

(%)

ASTM JIS
AM100A MC5 Al 10.0, Mn0.1 F 140 70 -
T4 240 70 6
T6 240 110 2
AM60A* MDC2A Al 6.0, Mn0.13
(AM60B:Cu<100ppm,
Ni<20ppm, Fe<50ppm)
F 220 130 8
AM60B* MDC2B
AM50A* - Al 5.0, Mn0.13
(Cu<100ppm, Ni<20ppm, Fe<40ppm)
F 210 125 10
AZ63A MC1 Al 6.0, Zn3.0, Mn0.15 F 180 70 4
T4 240 70 7
T5 180 80 2
T6 240 110 3
AZ91C MC2A

Al 8.7, Zn0.7, Mn 0.13

(AZ91E:Cu<150ppm, Ni<10ppm, Fe<50ppm)

F 160 70 .
AZ91E MC2B T4 240 70 7
T5 160 80 2
T6 240 110 3
AZ91A* MDC1A

Al 9.0, Zn2.0, Mn 0.10

(AZ91D:Cu<300ppm, Ni<20ppm, Fe<50ppm)

F 230 160 3
AZ91B* MDC1B
AZ91D* MDC1D
AZ92A MC3 Al 9.0, Zn 2.0, Mn 0.10 F 160 70 -
T4 240 70 6
T5 160 80 -
T6 240 130 -
AS41A* MDC3A Al 4.3, Si 1.0, Mn 0.35
(AS41B:Cu<200ppm, Ni<20ppm, Fe<35ppm)
F 210 140 6
AS41B*  
AE42* - Al 4.0, RE 2.7, Mn 0.13 F 230 145 10
ZK51A MC6 Zn 4.6, Zr 0.7 T5 240 140 5
ZK61A MC7 Zn 6.0, Zr 0.7 T5 270 180 5
T6 270 180 5
EZ33A MC8 RE 3.3, Zn 2.7, Zr 0.6 T5 140 100 2
ZE41A MC10 Zn 4.2, RE 1.2, Zr 0.7 T5 200 140 3
QE22A MC9 Ag 2.5, RE 2.1, Zr 0.7 T6 240 180 2
ZC63A - Zn 6.0, Cu 2.7, Mn 0.5 T6 210 125 4
WE54A - Y 5.2, RE 3.0, Zr 0.7 T6 250 172 2
WE43A - Y 4.0, RE 3.4, Zr 0.7 T6 250 165 2

注) *はダイカスト用合金である。機械的性質は鋳物材では最低値、ダイカスト材では標準的な値を示している。REは希土類元素である。AM60B、AM50A、AZ91D、AZ91E、AS41B合金は、耐食性の向上を目的として不純物Fe、Ni、Cuを極力少なくした高純度合金である。